|Place of Origin:||CHINA|
|Minimum Order Quantity:||200kg|
|Packaging Details:||Aï¼25kg/bucket B:18kg/bucket;A:230kg/bucket B:18kg/bucket|
|Supply Ability:||10000 KG MONTH|
|Color:||B WHITE||Component Of Basic Materials:||Polysiloxane|
|Density:||B 1.01||Viscosity:||B 20000|
|Mix Ratio By Weight (A:B):||10:1||Handing Curing Time:||3 MINS|
|Initial Curing Time:||20 MINS||Full Curing Time:||24 HOUR|
|Tensile Strength:||1.5 MPA||Elongation At Break:||250%|
|Hardness:||Shore A 39||Work Temperature:||-60-200|
Silicone Potting Compound,
potting compound for electronic components
4060F RTV Silicone Sealant for Auto Lamp assembly
â Product Features:
Ø 4060F (HT-360) RTV condensation type silicone adhesive sealing is a two-component, paste, black (gray) color, RTV silicone rubber.
Ø The room temperature fast curing, the release of ethanol molecules, no corrosion to the materials.
Ø With the two-component glue machine use, mature supporting scheme.
Ø After curing with excellent flexibility, resistance to alternating hot and cold resistant performance, aging resistance and electrical insulation properties, excellent moisture, earthquake resistance, corona resistance, anti leakage performance.
Ø This product does not need to use other primer, adhesive most materials such as metal, plastic, ceramic and glass, adhesive PP, PE needs to match a specific primer.
â Main Applications:
Ø The vehicle lamp shade for air tightness sealing adhesive, waterproof, dustproof sealing instrument, automobile and ship's windshield waterproof sealing.
â How to Use
Ø Before use, stir component A by hand or machine properly, keep component B sealed in the bucket and shake the bucket adequately.
Ø Check whether it’s adhering to Applied Materials theoretically.
Ø Mix component A and B with the mix ratio A: B=10:1 by weight. Beforehand simple tests are requested if you need to change the mix ratio.
Ø Vacuum defoaming is not necessary if the potting thickness is below 5mm, but it is requested if the thickness is more than 5mm.
Ø Heating curing is unsuited, or pinholes and blisters will occur.
Ø Long-term exposure of component B in the air is unsuited.
A: 25kg/bucket, B: 18kg/bucket.
A: 230kg/bucket, B: 18kg/bucket.
Ø Keep it away from children.
Ø Use it in ventilated places
Ø In case of contact with skins, wipe and then flush with clear water.
Ø In case of contact with eyes, flush with clear water immediately and go to hospital for checking.
Ø Store it in dry and shady places at the temperature of 8~28â
Ø Storage life: 6 months since the date of manufacture.
â Technical Data
|C omponent of Basic Materials||Polysiloxane|
|Density||Component A||g/cm 3||1.36|
|Mix Ratio by weight (A:B)||10:1|
|Handing Curing Time||min||3|
|Initial Curing Time||min||20|
|Full Curing Time||hour||24|
|Tensile Strength||After Curing||Mpa||1.5|
|Elongation at break||%||250|
|Volume Resistivity||Ω*cm||2.0x10 15|