Industrial Adhesive Glue
8664 Fast curing double component Industrial Adhesive Glue / fiberglass adhesive glue
8664 Fast curing double component Industrial Adhesive Glue / fiberglass adhesive glue
Product Details:
| Place of Origin: | China |
| Brand Name: | Huitian |
| Certification: | SGS |
| Model Number: | 8664 |
Payment & Shipping Terms:
| Minimum Order Quantity: | 100kg |
|---|---|
| Price: | Negotiation |
| Packaging Details: | A component:8664A4,4.4kg/bucket,4 bucket/box B component:8664B4,4kg/bucket,4 bucket/box |
| Delivery Time: | 8-15 days |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 100 ton month |
Product details
|
Detail Information |
|||
| A Component: | Polyhydric Alcohols | B Component: | Isocyanate |
|---|---|---|---|
| Viscosity: | B Component (3# Rotor20rpm)ï¼ 2000 2000±1000 MPa.s | Density(g/cm3): | B Componentï¼1.2±0.1g/cm3 |
| Pot Life(min): | >4 | Surface Drying Time(23±2â): | 4ï½10 Min |
| High Light: |
industrial epoxy adhesive,rtv silicone sealant |
||
Product Description
8664 Fast curing double component adhesive Used in metal, ceramic, cement, wood, ABS, PU, glass and Fiber glass
Product specificationTechnical Data Sheet
8664 Fast curing double component adhesive
8664
Curing fast, high bond strength, strength rises rapidly; environmental friendly, water resistance, low temperature resistance
No mildew, non-toxic, non-corrosive, excellent impact resistance and durability. Use to replace the
greatSmells, not environmentally friendly two-component acrylic adhesive.
Typical usage
Used in metal, ceramic, cement, wood, ABS, PU, glass and
Fiber glass and other materials, or mutual self-stick.
Characteristics before curing
Typical value range
Appearance
A component Gray to pale yellow paste
B component Light brown liquid
Base material chemical composition
A component polyhydric alcohols
B component Isocyanate
viscosity(mPa.s)
(GB/T2794-1995) Brookfield RVF
A component
(6# rotor50rpm): 9000 9000±3000mPa.s
B component
(3# rotor20rpm): 2000 2000±1000 mPa.s
density(g/cm3)
(GB/T13354-1992) 1.3 A component:1.3±0.1g/cm3
1.2 B component:1.2±0.1g/cm3
pot life(min) >4
surface drying time(23±2â) 6 4ï½10 min
After curing characteristics
Shear strength (Mpa)
23±2âsolidifytime 2h
(Al/Al) 7.0 ≥5
23±2âsolidify time7 days
(Al/Al) 11.5 ≥10
Working temperature(â) -40-90
Instructions
·Clean the surface to be bonded to be clean, dryï¼
·With glue visua
A:B
volume ratio1:1,Rapid mixing,A:B = 1:1 (V/V)
Accurate calibration scale= 1.1:1(W/W)ï¼
·Sizingtrial period is completed, the contact pressure is applied
·Room temperature curing or heat curing Curing
Attention:
·sizing ambient temperature 0 ~ 35 â, humidity <70%; unused glue should be closed immediately
store seal to prevent moisture absorption; highly contaminated glue cannot reload into the original packaging bucket
·keep away from children
·This product contains isocyanates substances which has the irritationon the skin andeyes. Recommended for use in a well-ventilated place
·In case of contact with eyes and skin, immediately rinse with water
·Product safety information, please refer to the product MSDS
packing specification
400ml/set, double-tubes
Storage conditions
Store in a cool dry place 8-28 â
Storage period: 12 months
special version
The data in this manual were obtained under laboratory conditions, the use of environmental differences, the user data and make reference to these
Conditions for analysis and testing.Huitian does not guarantee sales of our productsand use of the product and the specific conditions problem with the product.
We are not liable for any direct, indirect or incidental damages. Users in the course of any problems, you can return to Huitiantechnology and Service department, we will provide you with all the help.