Industrial glue Request a quote

Cyanoacrylate Adhesives

7603 Retaining anaerobict Cyanoacrylate Adhesives low viscosity , good oil content

7603 Retaining anaerobict Cyanoacrylate Adhesives low viscosity , good oil content

Product Details:

Place of Origin: China
Brand Name: Huitian
Certification: ISO
Model Number: 7603

Payment & Shipping Terms:

Minimum Order Quantity: 1000 pics
Price: Negotiation
Packaging Details: 50ml / bottle, 10 bottles / box. 250ml / bottle, 10 bottles / box
Supply Ability: 1000pics per day

Product details

Detail Information

Appearance: Green Liquid The Chemical Composition Of The Binder: Methacrylate
Name: 7603 Retaining Anaerobict Density: 1.10 1.00-1.15
Flash Point: 93 Fixed Time: ≤30
High Light:

cyanoacrylate adhesive glue


cyanoacrylate adhesive super glue

Product Description

7603 Retaining anaerobict, low viscosity, high strength, good oil content,

7603 Retaining anaerobic It is a single component, low viscosity, high strength, good oil content, excellent resistance to media holding anaerobic. The product between close fitting metal surfaces and cured and air separation.

Typical Applications

Radial clearance of 0.1mm in transition metal or interference fit within the hole and the shaft holding, may be slightly greasy surface use, room temperature can reach maximum intensity, can also play a role in sealing, easy to use.

Before solidification characteristics Typical values range

Appearance green liquid

The chemical composition of the binder methacrylate

Viscosity (mPa.s)

(GB / T2794-1995)

Brookfield RVT

2 # rotor 20 rpm 100-200

Density (g / cm3) 1.10 1.00-1.15

(GB / T13354-1992)

Flash Point (℃)> 93

(SH / T0733-2004)

Gap fill (mm) 0.10

Fixed time (min) ≤30

After curing characteristics

Full cure time at room temperature (h) 24

Static shear strength (MPa) 28 20-35

(GB / T18747.2)

Working temperature (℃) -50-150

Chemical / solvent resistance

Under the following conditions of aging and 22 ℃ testing.

Solvent Temperature (℃) have left initial strength ratio (%)

100h 500h 1000h

Oil 125 100 100 100

Leaded gasoline 251,009,085

Brake fluid 251,009,080

Ethanol 25100100100

Acetone 25,909,090

Water / glycol 871,009,080

(50% / 50%)


Cleaning hollow shaft mating surfaces to remove grease and dried, it recommended back to the days 7755 to improve the cleaning effect of the cleaning agent. Apply glue evenly with the site, gum in an amount sufficient to fill the gap, according to specifications fitted to the appropriate location. Best small gap sealing larger gaps will affect cure speed. In with the gap is large, it recommended back to the days 7769 accelerator to improve the sealing effect. To ensure maximum system pressure and resistance to media layer optimal performance, the curing time in more than 24 hours, in order to ensure the layer is completely cured.


Unused glue sealed for the next reuse. Highly contaminated glue can reload the original packaging bottle, the bottle so as not to affect the performance of the remaining glue.

Should not be used on plastics, should not be used in pure oxygen and oxygen-enriched systems, not for sealing chlorine or other strong oxidizing materials.

Store away from children.

This product contains acrylic and methacrylic acid esters, eye irritation to the skin. Recommended for use in a well-ventilated place.

In case of contact with eyes and skin, immediately rinse with water.

Product safety information, please refer to the product MSDS.

Packing specification

Order Code: 760301,50ml / bottle, 10 bottles / box, 80 bottles / box

760303,250ml / bottle, 10 bottles / box

Storage conditions

8-28 ℃ stored in a cool dry place.

Storage period of 18 months.